Effects of tungsten on erosion–corrosion behavior of high chromium white cast iron
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
Effects of tungsten on erosion–corrosion behavior of high chromium white cast iron
چکیده انگلیسی

In this study, effects of tungsten on wear resistance of high chromium white cast iron with and without tungsten in erosion–corrosion condition have been investigated. At the same time, the comparison between wear resistance of this grade of cast iron and low alloy steels with various contents of Cr which are used in industrial condition (in Sarcheshme Company, the greatest copper production company in the Middle East and with more than 4000 years historical cupper production background) was studied, while, copper concentrates have used for erosion particles. Results show that, because of higher hardness of matrix due to the tungsten, the wear resistance of high chromium cast iron increases. In addition to that, combine cutting and deformation wear mechanism and spalling mechanism were attributed in high chromium cast iron and low alloy steels, respectively. Subsequently, pitting mechanism in corrosion aspect was recognized because of inhomogeneity in chemical composition and sulfide inclusions content. Finally, the combine effects of erosion and corrosion (synergetic effect) were recognized in the high chromium white iron in industrial condition for the damaged samples.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volumes 454–455, 25 April 2007, Pages 623–628
نویسندگان
, , , ,