عنوان انگلیسی مقاله ISI
Magnetocaloric effect in pristine and Bi-doped Pr0.6Sr0.4MnO3 manganite
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Magnetocaloric effect in pristine and Bi-doped Pr0.6Sr0.4MnO3 manganite Magnetocaloric effect in pristine and Bi-doped Pr0.6Sr0.4MnO3 manganite](/preview/png/1591062.png)
چکیده انگلیسی
Near room temperature, magnetocaloric effect in pristine and Bi-doped Pr0.6Sr0.4MnO3 manganites has been studied using in-field heat capacity measurements. The Debye temperature (θD) for the pristine sample was estimated to be 522 K and its value increases to 530 K for the Bi-doped sample with x=0.05. The entropy associated with paramagnetic (PM) to ferromagnetic (FM) transition is found to be 2.4 J/mol K and 2.3 J/mol K for x=0 and 0.05 compositions respectively. The estimated values of adiabatic temperature âTad for the samples with x=0 and x=0.05 are respectively 2.2 K and 1.9 K for 0-6 Tesla. The maximum isothermal change in entropy, âSM for the sample Pr0.6Sr0.4MnO3 with transition temperature 306 K is found to be 2.7 J/kg-K with application of external magnetic field of 2 T and for Bi-doped sample (with x=0.05) the isothermal change in entropy reduces to 2.0 J/kg-K. The calculated maximum values of the isothermal entropy changes, âSM for the pristine sample, vary in the range 1.7-3.9 J/kg-K for a magnetic field change of 1-6 T. The present results suggest that these compounds can be possible candidates as magnetic refrigerants. This results in a large relative cooling power (RCP) around 93.5 J kgâ1 K for the pristine sample under an application of magnetic field of 2 T. On contrary, with Bi-doping, RCP decreases to 56 J kgâ1 K at external field of 2 T.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Solid State Communications - Volume 245, November 2016, Pages 65-69
Journal: Solid State Communications - Volume 245, November 2016, Pages 65-69
نویسندگان
Mamatha D. Daivajna, Ashok Rao,