Characteristics evolution of 6009/7050 bimetal slab prepared by direct-chill casting process

6009/7050 alloy bimetal slab was prepared by a direct-chill (DC) casting process. Homogenizing annealing, hot rolling and T6 treatment were successively performed and their effects on microstructure and properties of the slab were studied. The results reveal that the average diffusion layer thickness of as-cast slab, determined by interdiffusion of elements Zn, Cu, Mg and Si, was about 400 µm. Excellent metallurgical bonding was achieved because all tensile samples fractured on the softer 6009 alloy side after homogenizing annealing. After homogenizing annealing plus rolling, the average diffusion layer thickness decreased to 100 µm, while the network structure of 7050 alloy side transformed to dispersive nubby structure. Furthermore, subsequent T6 treatment resulted in diffusion layer thickness up to 200 µm and an obvious increase of the Vickers hardness for both 7050 and 6009 sides. The layered structure of the as-cast 6009/7050 bimetal is retained after hot rolling and T6 treatment.