Facile synthesis of hollow Cu2O polyhedron without template or etchant

• Novel hollow Cu2O polyhedrons were fabricated without template.
• Extensively observations were made to character the sample.
• Proposal the formation mechanism of the hollow polyhedron.

Previously, hollow Cu2O configurations have been fabricated with the use of template or etchant. However, in this study, simply mixing aqueous sodium dodecyl sulfate (SDS), CuCl2, NaOH, and NH2OH·HCl in the order listed, Cu2O polyhedron with empty interior arise, which is rarely reported. Observations made on the novel particles confirm the hollow polyhedral feature and reveal that the uniform particles exhibit a narrow size distribution at around 300–400 nm in diameter and ca. 50 nm in wall thickness. It was recorded that, upon the addition of reductant (NH2OH·HCl), the solution color changed orderly from light blue to green, yellow, and then orange within 1 h, while the basic mixture solution turned to acid immediately. We have reason to attribute the formation of hollow polyhedron to the surfactant role of SDS and the co-etching effect of oxidative etching and acidic etching, acting on dissolving Cu2O nanocrystals via oxidation with oxygen and reaction with HCl (from NH2OH·HCl).

In this letter, hollow Cu2O polyhedrons were successfully fabricated in a facile wet chemical system at room temperature without template or etchant.Figure optionsDownload as PowerPoint slide