A novel high thermal stability Ce3+-doped Ca5(SiO4)2F2 blue-emitting phosphor for near UV-excited white light-emitting diodes
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله
A novel high thermal stability Ce3+-doped Ca5(SiO4)2F2 blue-emitting phosphor for near UV-excited white light-emitting diodes
چکیده انگلیسی


• A novel blue-emitting Ca5(SiO4)2F2:Ce3+,Na+ phosphor was firstly prepared.
• XRD, PL, and thermal quenching properties were investigated.
• It shows very good thermal stability and quenching temperature is above 500 K.
• It shows a broadband absorption from 250 nm to 390 nm, which can match a near UV LED chip.

A novel high thermal stability Ca5(SiO4)2F2:Ce3+,Na+ blue-emitting phosphor was synthesized by solid-state reaction. The excitation spectrum shows a broad band extending from 200 nm to 390 nm, and the emission spectrum shows a broad blue band peaking at 408 nm with a half width of approximately 75 nm. The optimum doping concentration of Ce3+ is found to be 8 mol%. Its luminescence intensity at 420 K still kept by approximately 86% of the initial value at room temperature. The calculated CIE coordinates indicate that the phosphor has good color purity. Given their broadband absorption from 250 nm to 390 nm, these phosphors meet the application requirements for GaN-based light-emitting diodes.

Figure optionsDownload as PowerPoint slide

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Letters - Volume 160, 1 December 2015, Pages 5–8