• Ultrafine/nanocrystalline Al-based alloy was produced by copper mold casting.
• Hierarchical ultrafine-grained/nanocrystalline eutectic colonies were observed.
• It exhibits ultrahigh strength of 1.5 GPa and large ductility of 28%.
An in-situ ultrafine-grained/nanocrystalline Al-based bulk alloy with ultrahigh strength and large compressive plasticity has been produced by copper mold casting. According to the microstructural investigations, hierarchical ultrafine-grained/nanocrystalline eutectic colonies consisting of α-Al and Y3Al2 with homogeneously embedded Ag2Al nano-particles have been observed, besides few submicron-sized Al9Co2. The macroscopic and microscopic structural heterogeneities are able to achieve ultrahigh strength of ~1.5 GPa and large plasticity of ~28%, which are considered to be attributed to the hierarchical network of strengthening intermetallic phases combining with deformable α-Al solid solution suppressing the propagation of microcracks or shear bands. This may promote another perspective on designing and obtaining ductile ultrahigh-strength Al-based alloys.
Journal: Materials Letters - Volume 124, 1 June 2014, Pages 28–31