![عکس صفحه اول مقاله: One-step synthesis of hematite (α-Fe2O3) nano-particles by direct thermal-decomposition of maghemite One-step synthesis of hematite (α-Fe2O3) nano-particles by direct thermal-decomposition of maghemite](/preview/png/1649274.png)
In this research work, α-Fe2O3 nano-particles were prepared by direct thermal-decomposition of γ-Fe2O3. Precursor powders (γ-Fe2O3) were synthesized by wet chemical method at room temperature and then, the precursors were subsequently calcined in air for 1 h at 500 °C. Samples were characterized by thermal gravimetric analysis (TGA), X-ray diffraction (XRD), energy dispersive spectra (EDS), infrared spectrum (IR) and transmission electron microscopy (TEM), respectively. The XRD, EDS, and IR results indicated that the synthesized α-Fe2O3 particles were pure. The TEM image showed that the α-Fe2O3 nano-particles were spherical and 18 ± 2 nm in size. Magnetic properties have been detected by a vibrating sample magnetometer (VSM) at room temperature. The γ-Fe2O3 and α-Fe2O3 nano-particles exhibited a super-paramagnetic and weak ferromagnetic behavior at room temperature, respectively. Using the present method, hematite nano-particles can be produced without expensive organic solvent and complicated equipment.
Journal: Materials Letters - Volume 65, Issue 4, 28 February 2011, Pages 642–645