Fe-doped CoSb3 skutterudites were prepared by encapsulated induction melting and their thermoelectric and electronic transport properties were investigated. The positive signs of Seebeck and Hall coefficients for all Fe-doped specimens revealed that Fe atoms successfully acted as p-type dopants by substituting Co atoms. Carrier concentration increased with increasing Fe doping content and the Fe dopants could affect the electronic structure of CoSb3 and generate excess holes. However, carrier mobility decreased with increasing doping content, which indicates that the hole mean free path was reduced by the impurity scattering. Seebeck coefficient and electrical resistivity were almost independent of carrier concentration between 5.8 × 1019 and 2.0 × 1020 cm− 3 because the increase in carrier concentration by doping was competitive with the decrease in carrier mobility by the impurity scattering. Seebeck coefficient showed a positive value at all temperatures examined and it increased as the temperature increased. Temperature dependence of electrical resistivity suggested that Co1 − xFexSb3 is a highly degenerate semiconducting material. Thermal conductivity was considerably reduced by Fe doping and the lattice contribution was dominant in the Fe-doped CoSb3 skutterudites.
Journal: Materials Letters - Volume 61, Issues 11–12, May 2007, Pages 2446–2450