Pressureless-sintering behavior of nanocrystalline ZrO2–Y2O3–Al2O3 system

ZrO2–Y2O3–Al2O3 nanocrystalline powders have been synthesized using chemical coprecipitation method. Nano-powders were compacted uniaxially and densified in a muffle furnace. Densification studies showed that a fully dense pellet of ZrO2(3Y) and a 99% relative density for 5 mol% Al2O3 doped ZrO2(3Y) were obtained after sintering at 1200 °C. The presence of Al2O3 inhibits grain growth and suppresses the densification process. Full densification and the maximum microhardness of 17.8 GPa were achieved for the ZrO2(3Y)/5 mol% Al2O3 composites sintered at 1250 °C.