The combined effect of superficial nanocrystallisation by SMAT (Surface Mechanical Attrition Treatment) followed by plasma nitriding on the mechanical properties of a medical grade austenitic stainless steel was studied. SMAT conditions were optimised to enhance nitrogen diffusion. Experimental observations (energy dispersive X-ray spectroscopy profiles, cross-sectional optical micrographs, phase analysis by X-ray diffraction and micro-hardness profiles) show that polishing away a very thin layer after SMAT and before nitriding significantly improves nitrogen diffusion into the substrate, yielding a 50% thicker nitrided layer. Possible causes for this improvement are discussed.
► The formation of a nanocrystalline surface layer improves the nitrogen diffusivity.
► It yields a 50% thicker nitrided layer.
► This layer is 5 times harder than the 316L substrate.
► This result is obtained by adding a polishing step between SMAT and nitriding.
Journal: Surface and Coatings Technology - Volume 221, 25 April 2013, Pages 191–195