Microstructure and high temperature oxidation behavior of hot-dip aluminized coating on high silicon ductile iron

The oxidized graphite nodules resulted in cracks propagating in aluminide coating. Even though graphite nodules meant the existence of crack in the aluminide coating, the high temperature oxidation experiments indicated that the aluminide coating could prevent the oxidation of substrate effectively even at 750 °C.