High temperature tribological characterisation of TiAlSiN coatings produced by cathodic arc evaporation

This study reports on the wear properties at medium-high temperatures of TiAlSiN films deposited by cathodic arc evaporation on hot work steel substrates. The chemical composition and microstructure of the coatings were characterised by glow discharge optical emission spectroscopy, scanning electron microscopy and X-ray diffraction. The mechanical properties, i.e. hardness and elastic modulus were evaluated by nanoindentation, and the adhesion of the coatings was tested by scratch tests. Coatings with stoichiometries of Ti0.31Al0.1Si0.06N0.53 and Ti0.23Al0.12Si0.09N0.55 exhibit microstructures consisting of solid solutions of (Ti,Al,Si)N, where Al and Si replace Ti atoms. These films show high hardness and good adhesion strength to the hot work steels. Conversely, coatings with a stoichiometry of Ti0.09Al0.34Si0.02N0.55 show a wurtzite-like microstructure, low hardness and poor adhesion strength.The wear rates of the coatings were investigated by ball-on-disc experiments at room temperature, 200 °C, 400 °C and 600 °C, using alumina balls as counter surfaces. At room temperature, the films show wear rates of the same order of magnitude of TiN and TiAlN coatings. On the other hand, the wear rates of solid solution (Ti,Al,Si)N coatings measured at 200, and 400 °C are one order of magnitude smaller than those measured at room temperature due to the formation of oxide-containing tribofilms on the wear tracks. At 600 °C the wear rates increase but still keep smaller than those measured at room temperature, although this effect can be influenced by the softening of the steel substrates by over-tempering. EDS analyses revealed that, between 200 °C and 400 °C, the oxidation of the coating occurs only at the contact zone between the film and the counterpart body due to the sliding process.