A mechanical milling method was used for the deposition of TiN coatings. The principle of this method is that a substrate and powder were placed along with balls into the vibration chamber that was vibrated by a mechano-reactor. During mechanical milling process, the substrate surface was impacted by a large number of flying balls. The TiN particles trapped in between the balls and the substrate became cold welded to the surface. The repeated substrate-to-ball collisions forged TiN particles into a coating on the substrate surface. The process allowed the thick TiN coatings to be produced at room temperature in an ambient atmosphere. TEM study of the as-fabricated coatings was carried out. The coating formation depended on the size of the initial TiN particles. The 50-nm TiN nanoparticles were more easily cold welded than 1.5-μm microparticles. The nanoparticles had a tendency to consolidate and densify into the bulk material under the applied compressive loading. The TiN particles better consolidated and densified on the hard Ti surface than on the soft Al one.
Journal: Surface and Coatings Technology - Volume 203, Issue 13, 25 March 2009, Pages 1879–1884