Effects of nitrogen content on structure and mechanical properties of multi-element (AlCrNbSiTiV)N coating
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله
Effects of nitrogen content on structure and mechanical properties of multi-element (AlCrNbSiTiV)N coating
چکیده انگلیسی
AlCrNbSiTiV metallic and nitride films were deposited by reactive radio-frequency unbalanced magnetron sputtering. The composition, microstructure and mechanical properties of the coatings deposited at different nitrogen flow rates were evaluated. The deposited AlCrNbSiTiV metallic film has an amorphous structure. The nitride films, regardless of the nitrogen flow ratio, were found to have only an FCC structure register on the XRD profiles. A Stoichiometric nitride ratio, i.e. (Al,Cr,Nb,Si,Ti,V)50 N50 is attained for a nitrogen flow ratio (RN) of 10% and higher. At the lowest nitrogen flow ratio there is a preferred (200) orientation; however the films become less textured at higher nitrogen flow ratios. Nano-grained structures are obtained for all flow ratios, with grain sizes ranging from 8.7 to 12.3 nm. At the highest nitrogen flow rates the coatings have a compressive stress of around 4.5 GPa. The (Al,Cr,Nb,Si,Ti,V)50 N50 nitride coatings have both a high hardness and elastic modulus of 41 and 360 GPa, respectively. The maximum H/E ratio occurs at a nitrogen flow ratio of 20%.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 203, Issue 13, 25 March 2009, Pages 1891-1896
نویسندگان
, ,