Thermal stability behaviors of Cr(N,O)/CrN double-layered coatings by TGA/DTA analysis

In this study, Cr(N,O)/CrN double-layered coatings were synthesized using the cathodic arc deposition (CAD) process. CrN film was first deposited onto a substrate as an interlayer to ensure better adhesion, and Cr(N,O) film was subsequently deposited on top of the CrN layer as the surface layer. Variation in the Cr(N,O) coating composition was achieved through changing the O2/N2 flow ratio during the last stage of processing. Phase structure, chemical composition, and morphology of the resulting coatings were analyzed and observed using the X-ray diffractometer, Auger electron spectrometer and SEM. In addition, oxidation behavior of the coatings was investigated using TGA/DTA methods. The tests were carried out by increasing temperature up to 1000 °C in ambient air. With the introduction of oxygen gas during the CAD process, a superficial layer was produced in the Cr(N,O) constituent containing CrN and Cr2O3 phases. The formation of the oxide phase attributed to the reaction of chromium and oxygen was more favorable than that of chromium and nitrogen. The results also showed that Cr(N,O)/CrN double-layered coatings exhibited superior oxidation resistance at elevated temperature than that of CrN single-layer coated specimen (870 °C vs. 750 °C).