Surface wettability of polypropylene (PP) films has been significantly improved by the deposition of thin SiOx layers, elaborated from a mixture of hexamethyldisiloxane (HMDSO) and oxygen in a microwave DECR (distributed electron cyclotron resonance) plasma reactor (2.45 GHz, 400 W). Contact angle measurements, Atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS) were used to study, respectively, the change in surface free energy, surface topography and chemical composition due to the deposition of thin SiOx layers. Contact angle measurements revealed that the water contact angle value is reduced from about 99° for untreated PP surface to nearly 30° for coated PP film. The polar component of the surface energy is considerably increased from 0.5 to 35 mJ/m2. For films deposited in the presence of VUV photons, AFM images showed the growth of irregular structure due to substrate etching effect and the deconvolution results of the Si 2p XPS peaks indicated that the proportion of the partly oxidized silicon environment was the major component. However, for films deposited without the presence of VUV radiation, typical SiO2 agglomerates can clearly be seen on PP surface at a thickness of about 29 nm and the proportion of the silicon dioxide was the major component.
Journal: Surface and Coatings Technology - Volume 201, Issues 1–2, 12 September 2006, Pages 129–135