Ion-beam irradiation effects on reactively sputtered CrN thin films

The present study deals with CrN/Si bilayers irradiated at room temperature (RT) with 120 keV Ar ions. The CrN layers were deposited by d.c. reactive sputtering on Si(1 0 0) wafers, at different nitrogen partial pressures (2 × 10−4, 3.5 × 10−4 and 5 × 10−4 mbar), to a total thickness of 240–280 nm. The substrates were held at room temperature (RT) or 150 °C during deposition. After deposition the CrN/Si bilayers were irradiated up to fluences of 1 × 1015 and 1 × 1016 ions/cm2. Structural characterization was performed with Rutherford backscattering spectroscopy (RBS), cross-sectional transmission electron microscopy (XTEM) and grazing angle X-ray diffraction (XRD). For the highest nitrogen pressure (5 × 10−4 mbar) a pure stoichiometric CrN phase was achieved. The results showed that Ar ion irradiation resulted in the variation of the lattice constants, micro-strain and mean grain size of the CrN layers. The observed microstructural changes are due to the formation of the high density damage region in the CrN thin film structure.