Mid-frequency deposition of a-C:H films using five different precursors

The plasma-enhanced chemical vapour deposition (PECVD) of amorphous hydrogenated carbon films from pulsed discharges with frequencies in the range from 50 kHz to 250 kHz was investigated. Five different hydrocarbons (acetylene C2H2, isobutene C4H8, cyclopentene C5H8, toluene C7H8 and cycloheptatriene C7H8) were probed as film growth precursors. In addition, two types of pulse-generators with somewhat different waveforms were used to power the discharges in the so called mid-frequency range. The a-C:H films deposited in a parallel-plate reactor were characterised for their thickness/deposition rate, hardness and hydrogen content. The hydrogen concentration in the films varied between 19 at.-% and 37 at.-%. With the substrate temperature held constant, it is roughly in inverse proportion to the hardness. The film with the highest hardness of 25 GPa was formed at a deposition rate of 0.8 μm/h in the C2H2 discharge at the lowest investigated pressure of 2 Pa. With increasing molecular mass of the precursor mostly weaker films were deposited. Relatively high values of both deposition rate and hardness were achieved using the precursor isobutene: a hardness of 21 GPa combined with a deposition rate of 4.1 μm/h. From the probed precursors, isobutene is also most advantageous for a-C:H deposition at higher pressures (up to 50 Pa investigated). But, as an over-all trend, the a-C:H hardness decreases with increasing deposition rate.