Effect of high temperature post-oxidizing on tribological and corrosion behavior of plasma nitrided AISI 316 austenitic stainless steel

In this research, the microstructure, tribological and corrosion properties of plasma nitrided-oxidized AISI 316 austenitic stainless steel at high oxidation temperature were studied and compared with conventional plasma nitride. The structural, tribological and corrosion properties were analyzed using XRD, SEM, microhardness testing, pin-on-disk tribotesting and electrochemical polarization. Plasma nitriding was conducted for 5 h at 450 °C with gas mixture of N2/H2 = 1/3 to produce the S-phase. The nitrided samples were post-oxidized at 500 °C with gas mixture of O2/H2 = 1/5 for 15, 30 and 60 min. X-ray diffraction confirmed the development of CrN, ɛ and γ′ nitride phases and magnetite (Fe3O4) oxide phase under plasma nitriding-oxidizing process. In addition, it was found that oxidation treatment after plasma nitriding provides an important improvement in the friction coefficient and the corrosion resistance. The optimized wear and corrosion resistance of post-oxidized samples were obtained after 15 min of oxidation.