Cu surface segregation in Ni/Cu system

We report experimental evidence of Cu surface segregation in Ni/Cu system, during deposition of Ni film onto Cu substrate at room temperature and during heat treatment in vacuum. Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) by Tougaard's analysis results show that surface segregation defeats in competition with increase in Ni thickness and terminates when thickness of Ni increase to more than 4 nm. Surface energy and concentration were calculated using contact angle measurements and the results confirm that segregation reduces the surface energy. Surface segregation during heat treatment at 150–220 °C range as a function of time initially shows linear mass transfer. By solving Fick's equation and taking empirical diffusion coefficient, 125 ± 20 kJ/mol is obtained for activation enthalpy of effective diffusion.