Low-temperature deposition of iridium thin films by pulsed laser deposition

Extremely smooth iridium (Ir) thin films were deposited on Si(1 0 0) substrate at lower temperature than 300 °C by pulsed laser deposition (PLD) technique using Ir target in a vacuum atmosphere. The crystal orientation, surface morphology, and resistivity of the Ir thin films were systematically determined as a function of substrate temperature. Well-crystallized and single-phase Ir thin films with (1 1 1) preferred orientation were obtained at substrate temperature of 200–300 °C. The surface roughness increased with the increasing of substrate temperature. Likewise, the room-temperature resistivity of Ir thin films decreased with increasing substrate temperature, showing a low value of (10.7±0.1) μΩ cm at 300 °C.