Diffusion bonding of Fe-28Al(Cr) alloy with low-carbon steel in vacuum

Fe-28Al(Cr) alloy and low-carbon steel were diffusion bonded in a vacuum of 10−4–10−5 Pa. The relationship of the bond parameters and shear strength at the interface was discussed. Microstructure characteristics and the reaction products at the interface were investigated by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). The thickness of the diffusion reaction layer was measured with electron probe microanalysis (EPMA). The results indicated that controlling bonding temperature 1333 K for 3.6 ks, shear strength at the interface can be up to 112 MPa. Three kinds of reaction products were observed to have formed during the vacuum diffusion bonding, namely FeAl, Fe3Al and α-Fe (Al) solid solution. The thickness (X) of the diffusion reaction layer increases with bonding time (t) according to a parabolic law X2=6.4×103 exp(−104.1/RT)(t–t0) (μm2).