Radiation preparation of nano-powdered styrene-butadiene rubber (SBR) and its toughening effect for polystyrene and high-impact polystyrene

Nano-powdered styrene-butadiene rubber (NPSBR) was synthesized based on the styrene-butadiene rubber (SBR) latex via gamma radiation crosslinking followed by spray drying. Two functional monomers, 2-ethyl hexyl acrylate (2-EHA) and trimethylolpropane triacrylate (TMPTA) were used as crosslinking agents. It was found that both 2-EHA and TMPTA can improve the radiation crosslinking of SBR latex. Transmission electron microscope (TEM) and scanning electron microscope (SEM) revealed that the NPSBR has a particle size similar to that of SBR latex with a diameter of 100 nm due to the high degree of crosslinking of SBR. Mechanical testing results showed that NPSBR could toughen polystyrene (PS) and high-impact polystyrene (HIPS) effectively. In addition, NPSBR is more suitable to toughen HIPS than PS at low rubber content.