A mild method of amine-type adsorbents syntheses with emulsion graft polymerization of glycidyl methacrylate on polyethylene non-woven fabric by pre-irradiation

A mild pre-irradiation method was used to graft glycidyl methacrylate (GMA) onto polyethylene (PE) non-woven fabric (NF). The polymer was irradiated by electron beam in air atmosphere at room temperature. The degree of grafting (Dg) was determined as a function of reaction time, absorbed dose, monomer concentration and temperature. After 30 kGy irradiation, with 5% GMA, surfactant Tween 20 (Tw-20) of 0.5% at 55 °C for 15 min, the trunk polymer was made grafted with a Dg of 150%. Selected PE-g-PGMA of different Dg was modified with aminated compounds such as ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetetramine (TETA) and tetraethylenepentamine (TEPA). The obtained amine-type adsorbents were prepared to remove copper and uranium ions from solution. It was shown that at least 90% of copper and 60% of uranium with the initial concentration from 3 to 1000 ppb can be removed from water.

► GMA is successfully grafted onto PE non-woven fabric with a more mild pre-irradiation way air atmosphere at room temperature.
► With a Dg of 150%, it is modified by aminated compounds.
► The material can be used in the removal of copper and uranium ions from solution.