Effect of γ-irradiation on the thermomechanical and morphological properties of chitosan obtained from prawn shell: Evaluation of potential for irradiated chitosan as plant growth stimulator for Malabar spinach

In the present study we have synthesized chitosan from waste prawn shell via γ-irradiation of chitin and subsequent alkaline treatment. The detailed experimental studies demonstrated that nonirradiated chitin deacetylated by 40% NaOH solution showed 72% degree of deacetylation (DD), however 50 kGy irradiated chitin, deacetylated by 20% NaOH demonstrated 81.5% DD. Chitosan in solid state as obtained from γ-irradiation of chitin was further irradiated by different doses (2–100 kGy) of gamma irradiation and the effects of irradiation on the molecular weight, thermo-mechanical by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), and antimicrobial properties were evaluated with respect to nonirradiated chitosan sample. Gamma irradiation of chitosan with a dose of 100 kGy caused a decrease in average molecular weight from 1.9×105 to 6.5×104 Da and thus increased its solubility in water. Nonirradiated and γ-irradiated chitosan at concentration 1% (w/w) in water were prepared and used to evaluate of its potentiality for growth stimulation of Malabar spinach. The chitosan solution was sprayed on the specimen plants and neighboring soil where germinations were taken place and various plant growth parameters such as plant height, number of leaves, leaf areas, dry and wet weight of the plants and roots were investigated. The details study revealed that application of 30 kGy irradiated chitosan yielded 60% higher growth of the Malabar spinach than that obtained from nonirradiated chitosan. The data are consistent with preliminary results from field experiments and unambiguously confirms that a minor amount of chitosan has a profound effect on the growth and development of Malabar spinach.

Highlight
► A new approach for chitosan synthesis by γ-irradiation of chitin was described.
► Effect of irradiation on the various properties of chitosan was investigated.
► Irradiation causes scission of glycosidic linkage thus decrease of mw of chitosan.
► Irradiated increased water solubility & applied on Malabar spinach growth stimulation.
► Plant parameters showed 70% increased growth obtained by γ-irradiated chitosan.