• Ga/ZSM-5 prepared by post-modification in fluoride media.
• Comparative study of methanol and propanal conversion over Ga/ZSM-5.
• Ga/ZSM-5 have longer lifetime than parent ZSM-5 in methanol conversion.
• Post-modification doesn’t improve the ZSM-5 lifetime in propanal conversion.
• Feedstocks reactivity is the reason for difference reaction behavior.
Comparative study on catalytic conversion of methanol and propanal over Ga/ZSM-5 is reported in this paper. A series of Ga/ZSM-5 catalysts were obtained by post modification of ZSM-5 in a mixture of Ga(NO3)3 and NH4HF2. The obtained zeolite samples were subjected to detailed characterization and catalytic evaluation in methanol and propanal conversion reactions. It was found that the post-modification step by Ga(NO3)3 and NH4HF2 had effects both on structure and acidity: (1) decreasing both acid concentration and strength as indicated by NH3-TPD, FT-IR analysis and elemental analysis, (2) selective removing the defective zone of ZSM-5 zeolite, and (3) depositing Ga species on zeolite. The catalyst lifetime in methanol conversion reaction was dramatically improved after post-modification; the longest catalyst lifetime of Ga/ZSM-5-1 observed was 14 days. On the contrast, the catalyst lifetime in propanal conversion was kept constantly at 8 h over all zeolite samples. The different effects of zeolite after post-modification in methanol and propanal conversion are due to the reactivity difference between methanol and propanal.
Figure optionsDownload as PowerPoint slide
Journal: Fuel - Volume 168, 15 March 2016, Pages 68–75