Ultrafine anatase TiO2 nanoparticles produced in premixed ethylene stagnation flame at 1 atm

Nano-sized titanium oxide particles were synthesized in a stationary, laminar, premixed, stagnation flame burning an ethylene–oxygen–argon mixture at an equivalence ratio of 0.36 under the atmospheric pressure. The titanium precursor, titanium tetraisopropoxide (TTIP), was fed into the flame by a carrier argon flow through a heated TTIP bath. Particles synthesized in this flame were characterized for their size distribution, morphology, phase purity, and crystal structure, by scanning mobility particle sizer, transmission electron microscopy, and X-ray diffraction. It was found that the mean diameter of the particles was highly controllable and ranged from 3 to 6 nm depending on TTIP loading. The particle size was nearly uniform, and particles appeared to be single crystals without excessive aggregation. XRD analyses show that particles directly synthesized in the flame are pure anatase. Upon sintering and size growth on the flame stabilizer, a notable portion of particles transformed into rutile with much larger crystal sizes.