Effect of mineral admixtures and curing periods on shrinkage and cracking age under restrained condition

This paper presents the test results on cracking behavior at medium age of uniaxially restrained specimens containing different types of mineral admixture, namely fly ash and limestone powder. In this study, the uniaxially restrained shrinkage, free shrinkage and strength tests were conducted to study the potential of cracking of concrete under restrained shrinkage condition. The influences of water to binder ratio, mineral admixtures and curing period of concrete on cracking behavior were investigated in this study. The investigation showed that cracking age and cracking strain of restrained specimens vary with mix proportion, mineral admixture and curing period. The potential of shrinkage cracking is not influenced only by cracking strain and amount of shrinkage but also on shrinkage rate and tensile creep. Mixture with lower water to binder ratio (w/b = 0.35) shows shorter cracking age than the mixture with higher water to binder ratio (w/b = 0.55). Fly ash and limestone powder significantly increase cracking age of concrete. The cracking age increases with the increase of the replacement ratio of fly ash. The higher shrinkage rate, when exposed to drying, of mixture with longer curing period leads to shorter cracking age.