Numerical investigation of ductile crack growth behavior in a dissimilar metal welded joint

In this paper, the finite element method (FEM) based on GTN model is used to investigate the ductile crack growth behavior in single edge-notched bend (SENB) specimens of a dissimilar metal welded joint (DMWJ) composed of four materials in the primary systems of nuclear power plants. The J–Δa resistance curves, crack growth paths and local stress–strain distributions in front of crack tips are calculated for eight initial cracks with different locations in the DMWJ and four cracks in the four homogenous materials. The results show that the initial cracks with different locations in the DMWJ have different crack growth resistances and growth paths. When the initial crack lies in the centers of the weld Alloy182 and buttering Alloy82, the crack-tip plastic and damage zones are symmetrical, and the crack grow path is nearly straight along the initial crack plane. But for the interface cracks between materials and near interface cracks, the crack-tip plastic and damage zones are asymmetric, and the crack growth path has significant deviation phenomenon. The crack growth tends to deviate into the material whose yield stress is lower between the two materials on both sides of the interface. The different initial crack locations and mismatches in yield stress and work hardening between different materials in the DMWJ affect the local stress triaxiality and plastic strain distributions in front of crack tips, and lead to different ductile crack growth resistances and growth paths. For the accurate integrity assessment for the DMWJ, the fracture toughness data and resistance curves for the initial cracks with different locations in the DMWJ need to be obtained.

► Ductile crack growth behavior in a dissimilar metal welded joint was simulated.
► Interface crack growth tends to deviate into material with lower yield stress.
► Crack locations and mismatches affect local stress–strain distribution.
► Local stress–strain leads to different crack growth resistances and paths.