Effects of Calcium Silicate–based Materials on the Flexural Properties of Dentin
موضوعات مرتبط
علوم پزشکی و سلامت پزشکی و دندانپزشکی دندانپزشکی، جراحی دهان و پزشکی
پیش نمایش صفحه اول مقاله
Effects of Calcium Silicate–based Materials on the Flexural Properties of Dentin
چکیده انگلیسی

IntroductionProlonged exposure of root dentin to calcium hydroxide alters the fracture resistance of dentin. Calcium silicate–based materials (CSMs) used in endodontics release calcium hydroxide on setting. This study examined whether prolonged contact of dentin with CSMs adversely affects its mechanical properties.MethodsDentin beams prepared from extracted human molars (7 × 3 × 0.3 mm) were divided into 3 groups on the basis of the material to which dentin was exposed (Biodentine, MTA Plus, and untreated control beams). Three-point flexure to failure was performed for each beam at designated exposure times (24 hours, 1, 2, and 3 months; n = 10). Data were analyzed with 2-factor repeated-measures analyses of variance to determine the effects of material and aging time on flexural modulus, flexural strength, and modulus of toughness (α = 0.05).ResultsFor flexural modulus, there was no significant difference for material (P = .947) or aging time (P = .064) when compared with baseline control. For flexural strength, significant differences were associated with aging time (P < .001) but not with material (P = .349). Flexural strength of dentin exposed to Biodentine decreased significantly after 2 and 3 months, whereas that exposed to MTA Plus decreased significantly after 3 months of aging (P < .05). For modulus of toughness, significant declines were observed for both material (P < .004) and aging time (P < .001).ConclusionsBoth CSMs alter material toughness more than the strength and stiffness of dentin after aging in 100% relative humidity. Because dentin toughness is attributed to its collagen matrix, the amount of collagen extracted from mineralized dentin and changes in collagen ultrastructure should be further examined after exposure of dentin to CSMs.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Endodontics - Volume 38, Issue 5, May 2012, Pages 680–683
نویسندگان
, , , , , , , , ,