Capping a Pulpotomy with Calcium Aluminosilicate Cement: Comparison to Mineral Trioxide Aggregates
ترجمه فارسی عنوان
پوشش پالپوتومی با سیمان آلومینو اسید سیلیکا کلسیم: در مقایسه با مواد معدنی سه اکسید
کلمات کلیدی
سیمان آلومینات کلسیم / آلومینو اسید سیلیکات، سیلیکات کلسیم، اندودونتیک، کلرید معدنی تریاکسید، درد، تری کلسیم سیلیکات
موضوعات مرتبط
علوم پزشکی و سلامت پزشکی و دندانپزشکی دندانپزشکی، جراحی دهان و پزشکی
چکیده انگلیسی

IntroductionCalcium aluminate cements have shown little affinity for bacterial growth, low toxicity, and immunogenicity when used as a restoration material, but calcium aluminate cements have not been tested in vivo in pulpotomy procedures.MethodsTo address this question, a calcium aluminosilicate cement (Quick-Set) was tested along with 2 mineral trioxide aggregates, ProRoot MTA and MTA Plus. These cements were used as a capping agent after pulpotomy. Control rats had no pulpotomy, or the pulpotomy was not capped. Proinflammatory cytokines interleukin (IL)-1β and IL-1α were measured, and histology was performed at 30 and 60 days after capping. The nociceptive response was determined by measuring the lengthening of the rat's meal duration.Resultsand Conclusions: IL-1β and IL-1α concentrations were reduced in the capped teeth, but no differences were observed among the 3 cements. Dentinal bridging could be detected at both 30 and 60 days with each of the 3 cements, and the pulps were still vital 60 days after capping. Meal duration significantly shortened after placement of the 3 different cements, indicating a nociceptive response, but there were no differences among the materials. Calcium aluminosilicate cement had similar properties to mineral trioxide aggregates and is a viable option for pulpotomy procedures.