The fluorine-modified Mg–Al mixed oxides were synthesized by thermal decomposition of the fluorine-containing Mg–Al hydrotalcites, and their physicochemical properties were characterized by ICP, TGA, XRD, FTIR, CO2-TPD and N2 adsorption/desorption techniques. It was found that weak basic sites were gradually transformed into moderate and strong basic sites during thermal decomposition, and thus weak basic sites (OH− groups), moderate basic sites (Mg–O, Mg–F and Al–O pairs) and strong basic sites (coordinatively unsaturated F− and O2− ions) were all produced in the as-prepared samples. Furthermore, the basicity of moderate basic sites could be controlled by the change of fluorine content, which caused the change in the amounts of Mg–F pairs. In the synthesis of propylene glycol methyl ether from methanol and propylene oxide, the base-catalytic performance of the obtained samples was shown to be closely associated with their moderate basic sites.
Some fluorine-modified Mg–Al mixed oxides could be prepared by thermal decomposition of the fluorine-containing Mg–Al hydrotalcite. The weak, moderate and strong basic sites were all produced in the as-prepared samples. Moreover, the amount of basic sites could be controlled by the changes of decomposition temperature and fluorine content.Figure optionsDownload high-quality image (96 K)Download as PowerPoint slide
Journal: Applied Catalysis A: General - Volume 377, Issues 1–2, 1 April 2010, Pages 107–113