Immobilization of MSWI fly ash through geopolymerization: Effects of water-wash

The present research explored the role played by water-wash on geopolymerization for the immobilization and solidification of municipal solid waste incineration (MSWI) fly ash. The water-wash pretreatment substantially promoted the early strength of geopolymer and resulted in a higher ultimate strength compared to the counterpart without water-wash.XRD pattern of water-washed fly ash (WFA) revealed that NaCl and KCl were nearly eliminated in the WFA. Aside from geopolymer, ettringite (Ca6Al2(SO4)3(OH)12·26H2O) was formed in MSWI fly ash-based geopolymer (Geo-FA). Meanwhile, calcium aluminate hydrate (Ca2Al(OH)7·3H2O), not ettringite, appeared in geopolymer that was synthesized with water-washed fly ash (Geo-WFA). Leached Geo-WFA (Geo-WFA-L) did not exhibit any signs of deterioration, while there was visual cracking on the surface of leached Geo-FA (Geo-FA-L). The crack may be caused by the migration of K+, Na+, and Cl− ions outside Geo-FA and the negative effect from crystallization of expansive compounds can not be excluded. Furthermore, transformation of calcium aluminate hydrate in Geo-WFA to ettringite in Geo-WFA-L allowed the reduction of the pore size of the specimen. IR spectrums suggested that Geo-WFA can supply more stable chemical encapsulation for heavy metals.Static monolithic leaching tests were conducted for geopolymers to estimate the immobilization efficiency. Heavy metal leaching was elucidated using the first-order reaction/diffusion model. Combined with the results from compressive strength and microstructure of samples, the effects of water-wash on immobilization were inferred in this study.