Effect of pre-extraction on soda-anthraquinone (AQ) pulping of rice straw

The effect of hot-water and alkaline pre-extraction of rice straw on soda-anthraquinone pulping was carried out. The pre-extraction with hot water at 150 °C for 1 h dissolved 34.7% biomass and the pre-extracted liquor comprised of 16.6% sugars, 6.7% lignin, 6.6% acetic acid and other unknown products. But the pre-extraction with 1% NaOH at 100 °C for 1 h dissolved 10.2% sugars, 5.1% lignin and 10% acetic acid from rice straw. Pre-extracted rice straw was cooked by soda-anthraquinone process with varying alkali charges. The pulp from pre-extracted rice straw was low in kappa number with reduced pulp yield. The drainage resistance (°SR) improved obviously on pre-extraction of rice straw. Pulp strength properties such as the tensile index and the burst index were found to be lower, but the tear index was higher both with hot-water and alkaline pre-extraction. After bleaching, the gaps of the overall pulp yield and strength properties between pre-extracted and non-extracted rice straw became narrower. The alkaline pre-extraction showed improved yield and properties compared with hot-water pre-extracted rice straw.

► This paper deals with the pre-extraction of rice straw prior to pulping in order to remove fines, which improve the drainage resistance of the produced pulp.
► Dissolved materials from the rice-straw in the pre-extracted liquor can be used in producing biomaterials and fuels, which will help to replace fossil fuel.
► Pulp produced from the pre-extracted rice straw showed almost similar strength properties.
► Bleachability of the produced pulp is almost similar.