Crack propagation and flexural behaviour of RC beams under simultaneous sustained loading and steel corrosion
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی عمران و سازه
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
This paper investigated the cracking behaviour and flexural capacity of beams under simultaneous sustained loading and steel corrosion. Chloride ions were electro-migrated into the concrete beams, and then DC current, coupled with wetting and drying cycles, was applied to accelerate the steel corrosion. During the steel corrosion, the beams were subjected to sustained loading at different levels. The cracking maps were drawn and crack width was measured periodically. The flexural capacity and the steel corrosion degree were measured after seven wetting and drying cycles. The results show that simultaneous loading and corrosion lead to more severe and faster cracking damage on the beams and reduce the beams' ductilities. The corrosion of the tension reinforcement occurs more slowly than that of the stirrups, while the tension-reinforcement corrosion at the areas connecting with the stirrups is slighter than the corrosion at the other parts of the tension reinforcement.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Construction and Building Materials - Volume 151, 1 October 2017, Pages 208-219
Journal: Construction and Building Materials - Volume 151, 1 October 2017, Pages 208-219
نویسندگان
Jianfeng Dong, Yuxi Zhao, Kun Wang, Weiliang Jin,