عنوان انگلیسی مقاله ISI
Effects of TiC content on microstructure, mechanical properties, and thermal conductivity of W-TiC alloys fabricated by a wet-chemical method
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی انرژی
مهندسی انرژی و فناوری های برق
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effects of TiC content on microstructure, mechanical properties, and thermal conductivity of W-TiC alloys fabricated by a wet-chemical method Effects of TiC content on microstructure, mechanical properties, and thermal conductivity of W-TiC alloys fabricated by a wet-chemical method](/preview/png/4921084.png)
چکیده انگلیسی
W-(0-0.9)TiC (wt.%) alloys were prepared by a wet-chemical method and spark plasma sintering. The effects of TiC content on the microstructures, mechanical properties, and thermal conducting properties of the prepared W-TiC alloys were investigated. The results revealed that the average grain size of the W-(0-0.9)TiC alloys decreased, and their average TiC particle size increased with the increase of TiC content. The bending fracture strengths of the prepared samples increased significantly with increased TiC content in the range of 0-0.5%, which was attributed to the uniform distribution of TiC particles with a high proportion located in the tungsten grain interiors. The W-0.5TiC alloy exhibited the best mechanical properties with the highest relative density, bending strength, and flexural strain of 97.61%, 1065.72Â MPa, and 1.23%, respectively. Moreover, the thermal conductivities of the W-(0.1-0.5)TiC alloys were slightly lower than those of pure tungsten at all testing temperatures. However, the mechanical properties and thermal conducting properties of the W-0.7TiC and W-0.9TiC alloys were significantly deteriorated due to the non-uniform aggregation of TiC particles at the tungsten grain boundaries.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Fusion Engineering and Design - Volume 121, October 2017, Pages 366-372
Journal: Fusion Engineering and Design - Volume 121, October 2017, Pages 366-372
نویسندگان
Shaoting Lang, Qingzhi Yan, Ningbo Sun, Xiaoxin Zhang, Changchun Ge,