• MCF loaded copolymer was fabricated with a 3D opening cellular structure.
• MCF–copolymer supported sulfonic acid was accomplished via sulfonation.
• High catalysis activity was obtained in hydrolysis of natural fibers.
Mesocellular silicon foam supported poly(chloromethylstyrene-co-divinylbenzene) (MCF–copolymer) was synthesized. It has a pore size of 24.2 nm. The pore volume and the surface area were 0.84 cm3/g and 246.9 m2/g, respectively. MCF–copolymer supported sulfonic acid was accomplished via sulfonation with concentrated sulfuric acid. The acid amount on the MCF–copolymer was 2.03 mmol/g. Hydrolysis of banana pseudo-stem fibers and microcrystalline cellulose was carried out over the catalyst. The large pore size favors the diffusion of molecules in catalyzing bulky molecules. The corresponding catalytic turnover frequencies (TOF) were 5.57 h− 1 and 8.066 h− 1.
Figure optionsDownload as PowerPoint slide
Journal: Catalysis Communications - Volume 71, 5 November 2015, Pages 56–60