![عکس صفحه اول مقاله: Change of Crystallographic Orientation Characteristics of (001)-Oriented Electrodeposited Silver Films During Self-Annealing at Room Temperature Change of Crystallographic Orientation Characteristics of (001)-Oriented Electrodeposited Silver Films During Self-Annealing at Room Temperature](/preview/png/5029187.png)
Self-annealing behaviors of the electrodeposited silver films which preferentially orient in the (001) direction were investigated by in situ EBSD analysis. Self-annealing started in storage for a few hours at room temperature (R. T.) and was almost complete after storage for 6Â h at R. T. In the initial stage of self-annealing, recrystallization of (001)-oriented grains progressed with the formation of twins with (212) orientation. Membrane stress in the as-electrodeposited film was compression stress of approximately 20Â MPa. The compression membrane stress seems to become driving force for self-annealing of the (001)-oriented electrodeposited silver film. Membrane stress in the film changed from compression stress to tensile stress by recrystallization in self-annealing.
Journal: Procedia Engineering - Volume 184, 2017, Pages 725-731