عنوان انگلیسی مقاله ISI
Storage fading of a commercial 18650 cell comprised with NMC/LMO cathode and graphite anode
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Storage fading of a commercial 18650 cell comprised with NMC/LMO cathode and graphite anode Storage fading of a commercial 18650 cell comprised with NMC/LMO cathode and graphite anode](/preview/png/5149522.png)
چکیده انگلیسی
In this study, the storage capacity fade of a commercial 18650 lithium ion cell comprised with a composite cathode of LiNi0.5Mn0.3Co0.2O2 (NMC) and Li1.1Mn1.9O4 (LMO) and graphite anode at various depths-of-discharge (DoDs) and temperatures have been investigated. The results manifest that the capacity fading is strongly affected by the storage temperature and becomes prominent as temperatures higher than 45 °C. Results of the incremental capacity analysis of the charging/discharging curves cycled at C/25 rate under 25 °C after cells been stored at various DoDs at 60 °C for various durations are used to reveal the factors of storage capacity fade of this commercial cell in company with the results of post-mortem studies on the electrodes harvested from the 12 month storage-aged cells with SEM, EDX, XPS, XRD, and electrode capacity retention study with those of a fresh commercial cell for comparison. The contributions of these factors are also estimated quantitatively. The losses of active electrode materials are the main reasons of the storage capacity fade of the commercial cell comprised with composite NMC/LMO cathode and graphite anode, while the loss of lithium inventory is less influential. The degradation of the electrodes and the loss the lithium inventory are strongly DoD dependent.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Power Sources - Volume 349, 1 May 2017, Pages 27-36
Journal: Journal of Power Sources - Volume 349, 1 May 2017, Pages 27-36
نویسندگان
She-huang Wu, Po-Han Lee,