Effect of periodic surface cracks on the interfacial fracture of thermal barrier coating system

► The effect of multiple surface cracks on interfacial delamination is significant. ► Normalized critical surface crack spacing is an important parameter. ► Steady state does not exist in the case of small surface crack spacing. ► Appropriately high surface crack density can enhance the durability of TBC.