The electroplated Pd-Co alloy film on 316Â L stainless steel and the corrosion resistance in boiling acetic acid and formic acid mixture with stirring

Pd-Co alloy films were deposited on 316 L stainless steel by electroplating. Scanning electronic microscopy, X-ray photoelectron spectroscopy, X-ray diffraction, weight loss test and polarization test were used to determine the properties of the Pd-Co alloy films. The Pd-Co films show fine grain size, low porosity and obviously high micro-hardness. The Co content in the film can be controlled in a large range from 21.9 at.% to 57.42 at.%. Pd is rich on the Pd-Co film surface, which is benefit to increase the corrosion resistance. In boiling 90% acetic acid plus 10% formic acid mixture with 0.005 M Br− under stirring, the Pd-Co plated stainless steel samples exhibit evidently better corrosion resistance in contrast to Pd plated samples. The good corrosion resistance of the Pd-Co alloy film is explained by the better compactness, the lower porosity, and the obviously higher micro-hardness of the alloy films, which increases the resistance to erosion and retards the development of micro-pores in the film.