Tribological changes on SS304 stainless steel induced by nitrogen plasma immersion ion implantation with and without auxiliary heating

In order to achieve quite thick treated layers with reasonable thickness uniformity in SS304 steel, the plasma immersion ion implantation (PIII) process was run in high-temperature, up to 350 °C, to induce high thermal diffusion but avoid the white layer formation. In these experiments, we heated the sample-holder with a shielded resistive wire properly wound around it and subjected the SS samples to nitrogen glow discharge PIII with relatively low voltages (10 kV) in different temperatures. We also treated the SS samples by the traditional PIII method, slowly increasing the high voltage pulse intensities, until 14 kV at the end of processing, reaching temperatures of up to 350 °C. These modes of treatments were compared with respect to nitrogen implantation profiles, X-ray diffraction, tribology and mechanical properties. X-ray diffraction results indicated a much higher efficiency of auxiliary heated PIII mode compared to the ordinary PIII. Very prominent γN peaks were observed for the first mode, indicating large concentration of nitrogen in thick layers, confirmed by the nitrogen profiles measured by GDOS and AES. Improved mechanical and tribological properties were obtained for SS304 samples treated by the PIII with auxiliary heating, more than for ordinary PIII. Hardness was enhanced by up to 2.77 times, as seen by nanoindentation tests.