Evaluation of the barrier capability of Zr-Si films with different substrate temperature for Cu metallization

Barrier capability of Zr-Si diffusion barriers in Cu metallization has been investigated. Amorphous Zr-Si diffusion barriers were deposited on the Si substrates by RF reactive magnetron sputtering under various substrate temperatures. An increase in substrate temperature results in a slightly decreased deposition rate together with an increase in mass density. An increase in substrate temperature also results in grain growth as deduced from field emission scanning electron microscopy (FE-SEM) micrographs. X-ray diffraction (XRD) spectra and Auger electron spectroscopy (AES) depth profiles for Cu/Zr-Si(RT)/Si and Cu/Zr-Si(300 °C)/Si samples subjected to anneal at various temperatures show that the thermal stability was strongly correlated with the deposition temperature (consequently different density and chemical composition etc.) of the Zr-Si barrier layers. ZrSi(300 °C) with higher mass density make the Cu/Zr-Si(300 °C)/Si sample more stable. The appearance of Cu3Si in the Cu/Zr-Si/Si sample is attributed to the failure mechanism which may be associated with the diffusion of Cu and Si via the grain boundaries of the Zr-Si barriers.