Bismuth (Bi) thin films of different thicknesses were deposited onto Si(1 0 0) substrate at various substrate temperatures by thermal evaporation technique. Influences of thickness and deposition temperature on the film morphologies, microstructure, and topographies were investigated. A columnar growth of hexahedron-like grains with bimodal particle size distribution was observed at high deposition temperature. The columnar growth and the presence of large grains induce the Bi films to have large surface roughness as evidenced by atomic force microscopy (AFM). The dependence of the crystalline orientation on the substrate temperature was analyzed by X-ray diffraction (XRD), which shows that the Bi films have completely randomly oriented polycrystalline structure with a rhombohedral phase at high deposition temperature (200 °C) and were strongly textured with preferred orientation at low deposition temperatures (30 and 100 °C).
Journal: Applied Surface Science - Volume 253, Issue 14, 15 May 2007, Pages 5931-5938