Surface segregation in HAYNES 230 alloy

The surface segregation in the Ni-based alloy HAYNES 230 was studied by Auger Electron Spectroscopy and X-ray Photoelectron Spectroscopy between 400 and 1100 °C. The qualitative variations of the surface contents of S, P, W, Mo, N, Si, and Mn were determined as a function of annealing temperature and time. It was found that at 925 °C the maximum coverage of sulphur at the alloy surface is in the range 0.06-0.15 monolayers. Chromium evaporation from the HAYNES 230 surface under UHV conditions is clearly evidenced for annealing at 1100 °C.