![عکس صفحه اول مقاله: Epitaxial growth of Al on Si(1 1 1) with Cu buffer layers Epitaxial growth of Al on Si(1 1 1) with Cu buffer layers](/preview/png/5426867.png)
The structure of thin Al films grown on Si(1Â 1Â 1) with thin Cu buffer layers has been investigated using synchrotron radiation photoemission spectroscopy. A thin Cu(1Â 1Â 1) layer between the Si(1Â 1Â 1) substrate and an Al film may enhance quantum well effects in the Al film significantly. The strength of quantum well effects has been investigated qualitatively with respect to the thickness of the Cu buffer layer and to the Al film thickness. Deposition of Cu on Si(1Â 1Â 1)7Â ÃÂ 7 leads to formation of a disordered silicide layer in an initial regime before a well-ordered Cu(1Â 1Â 1) film is formed after deposition of the equivalent of 6 layers of Cu. In the regime below 6 layers of Cu the disorder is transferred to Al layers subsequently grown on top. The initial growth of up to 8 layers of Al on a well-ordered Si/Cu(1Â 1Â 1) layer leads to a disordered film due to the lattice mismatch between the two metals. When the Cu buffer layer and the Al over-layer are above 6 and 8 layers, respectively the Al film shows sharp low energy electron diffraction patterns and very sharp quantum well peaks in the valence band spectra signalling good epitaxial growth.
Journal: Surface Science - Volume 600, Issue 3, 1 February 2006, Pages 610-616