Properties of solution-processed MgInZnO semiconductor thin films and photodetectors fabricated at a low temperature using UV-assisted thermal annealing
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Ultraviolet (UV) irradiation-assisted thermal annealing is used for the fabrication of Mg doped InZnO (MIZO) semiconductor thin films and metal-semiconductor-metal (MSM) type photodetectors on alkali-free glasses at a low temperature of 300 °C. In this study, the effects of UV irradiation time on the structural features and the optical and electrical properties of sol-gel derived MIZO thin films were investigated, and the photoresponse properties of MIZO photodetectors fabricated using UV-assisted thermal annealing (UV-TA) and conventional thermal annealing (CTA) were compared. The molar ratio of In:Zn was fixed at 3:2, and the Mg content was maintained at 20 at% ([Mg]/[In+Zn]) in the precursor solution. After a spin-coating and drying procedure was performed twice, the dried sol-gel films were heated on a hotplate at 300 °C and exposed to UV irradiation in ambient air. The UV irradiation time was adjusted to 1, 2, 3, and 4 h. All annealed MIZO thin films had a dense microstructure, uniform film thickness, and flat surface and exhibited good optical transmittance (> 86.0%). The mean resistivity decreased with increasing irradiation time, and the samples irradiated for 4 h exhibited the lowest mean resistivity of 4.4Ã102 Ω-cm. Current-voltage (I-V) characteristics showed that the MIZO photodetectors operated in the photoconductive mode. Under illumination with UVC light, the MIZO photodetectors exhibited an Ilight-to-Idark ratio of 7.7 à 102 and had a photoresponsivity of 5.0 A/W at a bias of 5 V.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 15, 15 October 2017, Pages 11874-11878
Journal: Ceramics International - Volume 43, Issue 15, 15 October 2017, Pages 11874-11878
نویسندگان
Chien-Yie Tsay, Po-Hsien Wu,