Feasibility of producing geopolymer binder based on a brick clay mixture
ترجمه فارسی عنوان
امکان تولید باند ژئوپلیمر بر اساس مخلوط خاک رس آجر
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
چکیده انگلیسی
A brick clay mixture from a company localized in the north west of France is used for this study. The feasibility of producing geopolymer materials from a clay mixture was investigated. The final aim is to find a new application for this aluminosilicate material. One metakaolin (for a reference), the brick clay mixture, and the clay mixture calcined at two temperatures were compared after reaction with each of three alkaline solutions with different reactivity (the reactivity of each is defined). Physical, chemical, structural (FTIR and XRD) and thermal characterization (DTA) were first performed on the raw materials. Then, the structural evolution of the formed geopolymers was investigated using FTIR spectroscopy and XRD. Thus, this study demonstrates the feasibility of producing consolidated materials from a calcined brick clay (containing calcium oxides), which exhibits higher reactivity than brick clay. Plus, from a mixture of 25Â wt% of less reactive materials such as ground brick clay and 75Â wt% of reactive materials, it is possible to obtain geopolymer materials. FTIR study reveals the presence of a Ca2+ release phenomena, with a simultaneous polycondensation reaction for products based on calcined brick clay, which is different according to the silicate solution. Moreover, a link between [M++M2+] and the different networks formed in the samples based on calcined clay was found. Indeed, it appears that the concentration within the range 10.5-14Â mol/l favors the geopolymer network formation.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 13, September 2017, Pages 9860-9871
Journal: Ceramics International - Volume 43, Issue 13, September 2017, Pages 9860-9871
نویسندگان
Julie Peyne, Emmanuel Joussein, Jérôme Gautron, Julie Doudeau, Sylvie Rossignol,