Scintillation, TSL and RPL properties of MgF2 transparent ceramic and single crystal
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
Scintillation, TSL and RPL properties of MgF2 transparent ceramic and single crystal
چکیده انگلیسی
We have prepared MgF2 transparent ceramics by spark plasma sintering (SPS) and investigated the scintillation and dosimeter properties compared with those of a single crystal. Under X-ray irradiation, a transparent ceramic showed scintillation with a broad feature over 300-600 nm with decay times of 310 and 1940 μs while the single crystal did not show such emission. It was found that MgF2 show radio-photoluminescence (RPL), which is a generation of new luminescence center by ionizing radiation. The RPL was only observed in the transparent ceramic samples, which appeared as two emission bands peaking around 415 and 700 nm under 340±40 nm excitation. During the PL reading, the emission band at 415 nm effectively increased over 50 s. This result suggested that the RPL in MgF2 shows a build-up phenomenon. From PL emission/excitation characteristics and decay time, it was suggested that the RPL peak around 415 nm was due to M(C2h) center.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 9, 15 June 2017, Pages 7211-7215
نویسندگان
, , , , , ,