An investigation in to the mechanical properties of CP Ti/TiO2 nanocomposite manufactured by the accumulative roll bonding (ARB) process
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: An investigation in to the mechanical properties of CP Ti/TiO2 nanocomposite manufactured by the accumulative roll bonding (ARB) process An investigation in to the mechanical properties of CP Ti/TiO2 nanocomposite manufactured by the accumulative roll bonding (ARB) process](/preview/png/5438132.png)
چکیده انگلیسی
In this study, a commercially pure titanium (CP Ti) sheet was produced by the ARB process. Then, the mechanical properties of monolithic and nanocomposites specimens manufactured using 0.1, 0.3, and 0.5Â wt% TiO2 nanoparticles as the reinforcement were investigated at different ARB cycles. The results showed improvement in the mechanical properties of specimens with the addition of TiO2 nanoparticles, as their yield strength and ultimate tensile strength were increased by increasing the TiO2 nanoparticles percent. In this regard, the ultimate tensile strength of the monolithic specimen reached to 810Â MPa, while it was 980Â MPa, 1040Â MPa, and 1085Â MPa after applying 8 ARB cycles for 0.1Â wt%, 0.3Â wt% and 0.5Â wt% nanocomposite specimens, respectively. However, the ultimate tensile strength of the as-received CP Ti sheet was 285Â MPa. Moreover, the yield strength and the ultimate tensile strength were increased by increasing the number of ARB cycles and the total elongation; on the other hand, in the monolithic and nanocomposite specimens, it was decreased by increasing the number of ARB cycles. Grain refinements due to severe strain, work hardening and TiO2 nanoparticles reinforcements were the main causes accounting for the improved mechanical properties. Recovery and dynamic recrystallization were two phenomena observed via TEM studies in the ARB process, leading to the development of equiaxed grains in the final ARB cycles.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 1, Part A, January 2017, Pages 201-207
Journal: Ceramics International - Volume 43, Issue 1, Part A, January 2017, Pages 201-207
نویسندگان
J. Moradgholi, A. Monshi, K. Farmanesh,